Cage-Rearrangement

Reorganization of the siloxane cage-like core (T₈ → T₁₀) can be performed, including isolation of intermediates, and cage rearrangement achieved by using Bronsted superacid, trifluoromethanesulfonic acid (CF₃SO₃H). In this case, reaction of hexahedral silsesquioxane and CF₃SO₃H in DMSO conducted in 1 : 12 molar ratio gives heptahedral silsesquioxane. In the first step CF₃SO₃H acid attacks siloxane Si-O-Si bonds and the formation of Si-O-SO₂CF₃ bond parallel with cage opening process is observed and compound B is obtained (Figure below). Such an inversion is observed at silicon atom during nucleophilic displacement reaction that is usually noticed when leaving groups are replaced by soft nucleophiles. Uponfurther acid attack, both T₆(OH)₄ C and siloxane dimer D are formed. Because this reaction takes place in an aqueous conditions, compound E of general formula T₈(OH)₄ as a consequence of hydrolysis reaction was obtained. E is prone to reaction with D and due to this, the abstraction of CF₃SO⁻
₃ anion occurs and the closure frame with the spontaneous cage-rearrangement to heptahedral T₁₀ structure F is observed. Although, heptahedral F is less favorable energetically (MM2 data), in this case its creation is forces by the formation of a new Si₄O₄ moiety from much more less stable substrates D and E.^[8]

Reaction of OAS-POSS-Cl with CF₃SO₃H in DMSO. B-E constitute intermediates isolated during A → F cage-rearrangement.

Poly(phenylsilsesquioxane) does not adopt a cage structure, but is a polymer with a ladder-like repeating unit.

Polymeric silsesquioxanes

Polymeric silsesquioxanes have been reported, first by Brown. High molecular weight tractable polymeric phenyl silsesquioxane featured a ladder-type structure.^[9] Brown's findings were the basis for many future investigations. Brown's synthesis proceeded in three-steps: (1) the hydrolysis of phenyltrichlorosilane, (2) equilibration of this hydrolyzate with potassium hydroxide at a low concentration and temperature to give the prepolymer, and (3) equilibration of the prepolymer at a high concentration and temperature to give the final polymer. Other notable silsesquioxane polymers include the soluble polymethylsilsesquioxane with high molecular weights described by Japan Synthetic Rubber.^[10] This polymer which, unlike its phenyl derivative, gels easily during the course of its synthesis, has found applications in cosmetics,^[11] resins,^[12] and lithography.^[13] Hierarchical organic-inorganic (hybrid) polysilsesquioxane (PSQ) materials using polyhedral oligomeric silsesquioxanes (POSS) cages as singular building blocks of the inorganic framework were synthesized by different research groups, exhibiting high specific surface area and hydrothermal stability and micro and/or mesoporosity.^{[14][15][16][17]} In addition, Marchesi et al. developed a series of amorphous POSS-based polysilsesquioxanes, in which the POSS cages (of partially-condensed T₇-POSS or anionic completely-condensed T₈-POSS molecules) act as structural units of the polymer-like inorganic network, both alone^[18] or in conjunction with metal ions of the lanthanide series (europium and terbium, especially).^[19][20]

Hydridosilsesquioxanes

A well known hydrogen silsesquioxane is [HSiO_3/2]₈.^[21] Early syntheses involved treatment (protonation) of trichlorosilane with concentrated sulfuric acid, and fuming sulfuric acid, affording T₁₀-T₁₆ oligomers. The T₈ cluster was also synthesized by the reaction of trimethylsilane with a mixture of acetic acid, cyclohexane, and hydrochloric acid. The Si-H groups are amenable to hydrosilylation.^[22]

Electronic materials

Films of organosilsesquioxane, e.g., poly(methylsilsesquioxane), have been examined for semiconducting devices.^[23][24] Poly(hydridosilsesquioxane), which has a linked-cage structure, was sold under the name Fox Flowable Oxide.^[23]

Methylsilsesquioxanes have been examined for spin-on-glass (SOG) dielectrics. Bridged silsesquioxanes have been used for quantum confined nano-size semiconductors. Silsesquioxane resins have also been used for these applications because they have high dielectric strengths, low dielectric constants, high volume resistivities, and low dissipation factors, making them very suitable for electronics applications. These resins have heat and fire resistant properties, which can be used to make fiber-reinforced composites for electrical laminates.

Polyhedral oligomeric silsesquioxanes have been examined as a means to give improved mechanical properties and stability, with an organic matrix for good optical and electrical properties.^[25][26] The mechanisms of degradation in these devices is not well understood, but it is believed that material defect understanding is important for understanding the optical and electronic properties.

Hydridosilsesquioxanes can be converted to silica coatings for potential application in integrated circuits.^[27][28]

LEDs

For potential applications to light emitting diodes, cubic silsesquioxanes. have been functionalized.^[29] One of the first precursors used in light emitting application was octadimethylsiloxysilsesquioxane, which can be prepared in yields of >90% by treating tetraethoxysilane or rice hull ash with tetramethylammonium hydroxide followed by dimethylchlorosilane. The general method of hydrolyzing organotrichlorosilanes is still effective here. When brominated or aminated, these structures can be coupled with epoxies, aldehydes, and bromoaromatics, which enable attachment of these silsesquioxanes to π-conjugated polymers. These methods can use copolymerization techniques, Grignard reagents, and different coupling strategies. There has also been research on the ability of conjugated dendrimer silsesquioxanes to behave as light emitting materials. Though, highly branched substituents tend to have π-π interactions, which hinder high luminescent quantum yield.

Sensors

For chemosensor applications, silsesquioxane cages conjugated with fluorescent molecules can be directly used to detect fluoride ions under a cage-encapsulation showing a change of color under naked eyes ^[30] and other anions.^[31]

Antimicrobial silsesquioxanes

Silsesquioxanes have been functionalized with biocidal quaternary ammonium (QASs) groups to produce antimicrobial coatings. QASs are disinfectants, antiseptics, and antifoulants that kill bacteria, fungi, and algae.^[32][33] The relatively small size of the silsesquioxane molecule, 2-5 nm, allows a QAS functionalized molecule to have a charge density similar to dendrimers and thus the antimicrobial efficacy is prominent. Dimethyl-n-octylamine was quaternized by octa(3-chloropropylsilsesquioxane), (T-ClPr)₈.^[34] The resulting material exhibited antimicrobial efficacy for the prevention of growth of both Gram-positive and Gram-negative bacteria.

Array of QAS functionalized polyhedral oligomeric silsesquioxanes (Q-POSS) have been reported.^[35] These researchers varied the alkyl chain length from –C₁₂H₂₅ to –C₁₈H₃₇ and varied the counter ion between chloride, bromide, and iodine. The first reaction was the hydrosilylation between allydimethlamine and octasilane polyhedral oligomeric silsesquioxane via Karstedt's catalyst to make a tertiaryamino-functionalized silsesquioxane. The second step was the quaternization of the tertiaryamino groups with an alkyl halide. The alkyl halides used were 1-iodooctadecane, 1-bromohexadecane, and 1-chloroctadecane.

The silsesquioxane core in these hybrid materials provides an increased glass transition temperature, improved mechanical properties, higher use temperature, and lower flammability. These desirable properties combined with the ability to readily functionalize a silsesquioxane with multiple antimicrobial groups allows for robust biocides with higher charge densities while maintaining a compact molecular structure. The organic functionalities provide high compatibility with polymers allowing for easy incorporation into many mediums. Of particular interest are silicone paints and coatings used in hospitals. Typical biocidal ammonium functionalized polymers are incompatible, but silsesquioxanes closely mimic the silicone structure. A silicone-based paint combined with QAS-functionalized silsesquioxanes could be used to paint medical and sanitary devices, biomedical devices, exam equipment, medical storage rooms, hospital rooms, clinics, doctor offices, etc. to prevent the formation and spread of bacteria. For example, the Q-POSS developed was combined with polydimethylsiloxane and catalysis to form a crosslinked network.^[35] The researchers found that coatings based on bromide and chloride had the best antimicrobial efficacy.

Other partially condensed silsesquioxanes

Other partially condensed species adopt ladder structures wherein in which two long chains composed of RSiO_3/2 units are connected at regular intervals by Si-O-Si bonds. Amorphous structures include RSiO_3/2 unit connections without any organized structure formation.^[29]

Partially condensed silsesquioxane.

${\displaystyle {\begin{array}{ll}{\ce {{RSiZ3}+3H2O->{RSi(OH)3}+3HZ}}&{\text{hydrolysis}}\\{\ce {3RSi(OH)3->[{\text{cat.}}]3RSiO_{3/2}}}+4.5{\ce {H2O}}&{\text{condensation}}\\{\ce {{RSi(OH)3}+RSiZ3->[{\text{cat.}}]{2RSiO_{3/2}}+3HZ}}&{\text{condensation}}\\\mathrm {Z=OR',Cl,OAc} &{\text{cat. = catalyst}}\end{array}}}$

Scheme for the synthesis of silsesquioxanes.

Metal complexes of partially condensed silsesquioxanes and metal-containing POSS

The incompletely condensed silsesquioxanes bind numerous metals, including Na⁺, Li⁺, and Be²⁺ as well as transition metals.^[40][41][42] Cubic metal-silsesquioxane derivatives of the core stoichiometry MSi₇O₁₂ can be prepared by treating the incomplete cage with a metal halide in the presence of a base such as triethylamine.^[43] Another route of synthesis involves first deprotonating the trisilanol group using LiN(SiMe₃)₂.^[44] Aspinall et al. later succeeded in doing the same using three equivalents of n-BuLi in hexanes and further results indicate that alkali metal derivatives of deprotonated silsesquioxanes could also be prepared using alkali metalbis(trimethylsilyl) amides.^[40] Marchesi et. al synthesised a luminescent fully-condensed rare-earth-doped POSS bearing in the structure an europium ion by reaction of the open-corner heptaisobutyl trisilanol T₇-POSS ((C₄H₉)₇Si₇O₉(OH)₃) with anhydrous EuCl₃ under basic conditions.^[45] Furthermore, a combination of partially-condensed tetrasilanolphenyl POSS with terbium acetate and/or europium acetate (at different molar ratio with both metals) led to novel double-decker silsesquioxane (DDSQ) materials consisting of lanthanide-doped POSS units with intrinsic luminescent properties, in which the lanthanide ion(s) act as both structural and functional agents in the final compound.^[46]

Catalytic properties

Although lacking commercial applications, metallasilsesquioxanes have been investigated as catalysts. The coordination environment provided by Cy₇Si₇O₉(OH)₃ has been proposed to approximate β-tridymite and β-cristobalite. Some of these complexes are active as catalysts for alkene metathesis, polymerization, epoxidation and Diels-Alder reactions of enones, as well as other Lewis acid-catalyzed reactions like Oppenauer oxidation and Meerwein-Pondorf-Verley reductions. .^[47] A number of metallasilsesquioxanes have been reported that can polymerize ethene, akin to the Phillips catalyst.^[48] The catalyst can be easily activated with trimethylaluminum and typically proceeds with high turnover number.^[48] Vanadium complexes as well as Ziegler–Natta type catalysts also catalyze the polymerization of ethylene.^[49] The coordination of metals to the silsesquioxane framework gives electrophilic centers that are approximately as electron-withdrawing as a trifluoromethyl group, leading to increased catalytic activity.^[47]