Device efficiency

The efficiency of a thermoelectric device for electricity generation is given by ${\displaystyle \eta }$, defined as

$${\displaystyle \eta ={{\text{energy provided to the load}} \over {\text{heat energy absorbed at hot junction}}}.}$$

The maximum efficiency of a thermoelectric device is typically described in terms of its device figure of merit ${\displaystyle ZT}$ where the maximum device efficiency is approximately given by^[7]

$${\displaystyle \eta _{\mathrm {max} }={T_{\rm {H}}-T_{\rm {C}} \over T_{\rm {H}}}{{\sqrt {1+Z{\bar {T}}}}-1 \over {\sqrt {1+Z{\bar {T}}}}+{T_{\rm {C}} \over T_{\rm {H}}}},}$$

where ${\displaystyle T_{\rm {H}}}$ is the fixed temperature at the hot junction, ${\displaystyle T_{\rm {C}}}$ is the fixed temperature at the surface being cooled, and ${\displaystyle {\bar {T}}}$ is the mean of ${\displaystyle T_{\rm {H}}}$ and ${\displaystyle T_{\rm {C}}}$. This maximum efficiency equation is exact when thermoelectric properties are temperature-independent.

For a single thermoelectric leg the device efficiency can be calculated from the temperature dependent properties S, κ and σ and the heat and electric current flow through the material.^[8][9][10] In an actual thermoelectric device, two materials are used (typically one n-type and one p-type) with metal interconnects. The maximum efficiency ${\displaystyle \eta _{\mathrm {max} }}$ is then calculated from the efficiency of both legs and the electrical and thermal losses from the interconnects and surroundings.

Ignoring these losses and temperature dependencies in S, κ and σ, an inexact estimate for ${\displaystyle ZT}$ is given by^[1][5]

$${\displaystyle Z{\bar {T}}={(S_{p}-S_{n})^{2}{\bar {T}} \over [(\rho _{n}\kappa _{n})^{1/2}+(\rho _{p}\kappa _{p})^{1/2}]^{2}}}$$

where ${\displaystyle \rho }$ is the electrical resistivity, and the properties are averaged over the temperature range; the subscripts n and p denote properties related to the n- and p-type semiconducting thermoelectric materials, respectively. Only when n and p elements have the same and temperature independent properties (${\displaystyle S_{p}=-S_{n}}$) does ${\displaystyle Z{\bar {T}}=z{\bar {T}}}$.

Since thermoelectric devices are heat engines, their efficiency is limited by the Carnot efficiency ${\displaystyle {\frac {T_{\rm {H}}-T_{\rm {C}}}{T_{\rm {H}}}}}$, the first factor in ${\displaystyle \eta _{\mathrm {max} }}$, while ${\displaystyle ZT}$ and ${\displaystyle zT}$ determines the maximum reversibility of the thermodynamic process globally and locally, respectively. Regardless, the coefficient of performance of current commercial thermoelectric refrigerators ranges from 0.3 to 0.6, one-sixth the value of traditional vapor-compression refrigerators.^[11]

Power factor

Often the thermoelectric power factor is reported for a thermoelectric material, given by

$${\displaystyle \mathrm {Power~factor} =\sigma S^{2}[W/m/K^{2}]}$$

where S is the Seebeck coefficient, and σ is the electrical conductivity.

Although it is often claimed that TE devices with materials with a higher power factor are able to 'generate' more energy (move more heat or extract more energy from that temperature difference) this is only true for a thermoelectric device with fixed geometry and unlimited heat source and cooling. If the geometry of the device is optimally designed for the specific application, the thermoelectric materials will operate at their peak efficiency which is determined by their ${\displaystyle zT}$ not ${\displaystyle \sigma S^{2}}$.^[12]

Aspects of materials choice

For good efficiency, materials with high electrical conductivity, low thermal conductivity and high Seebeck coefficient are needed.

Bismuth chalcogenides and their nanostructures

Materials such as Bi
₂Te
₃ and Bi
₂Se
₃ comprise some of the best performing room temperature thermoelectrics with a temperature-independent figure-of-merit, ZT, between 0.8 and 1.0.^[22] Nanostructuring these materials to produce a layered superlattice structure of alternating Bi
₂Te
₃ and Sb
₂Te
₃ layers produces a device within which there is good electrical conductivity but perpendicular to which thermal conductivity is poor. The result is an enhanced ZT (approximately 2.4 at room temperature for p-type).^[23] Note that this high value of ZT has not been independently confirmed due to the complicated demands on the growth of such superlattices and device fabrication; however the material ZT values are consistent with the performance of hot-spot coolers made out of these materials and validated at Intel Labs.

Bismuth telluride and its solid solutions are good thermoelectric materials at room temperature and therefore suitable for refrigeration applications around 300 K. The Czochralski method has been used to grow single crystalline bismuth telluride compounds. These compounds are usually obtained with directional solidification from melt or powder metallurgy processes. Materials produced with these methods have lower efficiency than single crystalline ones due to the random orientation of crystal grains, but their mechanical properties are superior and the sensitivity to structural defects and impurities is lower due to high optimal carrier concentration.

The required carrier concentration is obtained by choosing a nonstoichiometric composition, which is achieved by introducing excess bismuth or tellurium atoms to primary melt or by dopant impurities. Some possible dopants are halogens and group IV and V atoms. Due to the small bandgap (0.16 eV) Bi₂Te₃ is partially degenerate and the corresponding Fermi-level should be close to the conduction band minimum at room temperature. The size of the band-gap means that Bi₂Te₃ has high intrinsic carrier concentration. Therefore, minority carrier conduction cannot be neglected for small stoichiometric deviations. Use of telluride compounds is limited by the toxicity and rarity of tellurium.^[24]

Lead tellurides

Heremans et al. (2008) demonstrated that thallium-doped lead telluride alloy (PbTe) achieves a ZT of 1.5 at 773 K.^[25] Later, Snyder et al. (2011) reported ZT~1.4 at 750 K in sodium-doped PbTe,^[26] and ZT~1.8 at 850 K in sodium-doped PbTe_1−xSe_x alloy.^[27] Snyder's group determined that both thallium and sodium alter the electronic structure of the crystal increasing electronic conductivity. They also claim that selenium increases electric conductivity and reduces thermal conductivity.

In 2012 another team used lead telluride to convert waste heat to electricity, reaching a ZT of 2.2, which they claimed was the highest yet reported.^[28][29]

Inorganic clathrates

Inorganic clathrates have the general formula A_xB_yC_46-y (type I) and A_xB_yC_136-y (type II), where B and C are group III and IV elements, respectively, which form the framework where “guest” A atoms (alkali or alkaline earth metal) are encapsulated in two different polyhedra facing each other. The differences between types I and II come from the number and size of voids present in their unit cells. Transport properties depend on the framework's properties, but tuning is possible by changing the “guest” atoms.^[30][31][32]

The most direct approach to synthesize and optimize the thermoelectric properties of semiconducting type I clathrates is substitutional doping, where some framework atoms are replaced with dopant atoms. In addition, powder metallurgical and crystal growth techniques have been used in clathrate synthesis. The structural and chemical properties of clathrates enable the optimization of their transport properties as a function of stoichiometry.^[33][34] The structure of type II materials allows a partial filling of the polyhedra, enabling better tuning of the electrical properties and therefore better control of the doping level.^[35][36] Partially filled variants can be synthesized as semiconducting or even insulating.^[37]

Blake et al. have predicted ZT~0.5 at room temperature and ZT~1.7 at 800 K for optimized compositions. Kuznetsov et al. measured electrical resistance and Seebeck coefficient for three different type I clathrates above room temperature and by estimating high temperature thermal conductivity from the published low temperature data they obtained ZT~0.7 at 700 K for Ba₈Ga₁₆Ge₃₀ and ZT~0.87 at 870 K for Ba₈Ga₁₆Si₃₀.^[38]

Compounds of Mg and group-14 element

Mg₂B^IV (B¹⁴=Si, Ge, Sn) compounds and their solid solutions are good thermoelectric materials and their ZT values are comparable with those of established materials. The appropriate production methods are based on direct co-melting, but mechanical alloying has also been used. During synthesis, magnesium losses due to evaporation and segregation of components (especially for Mg₂Sn) need to be taken into account. Directed crystallization methods can produce single crystals of Mg₂Si, but they intrinsically have n-type conductivity, and doping, e.g. with Sn, Ga, Ag or Li, is required to produce p-type material which is required for an efficient thermoelectric device.^[39] Solid solutions and doped compounds have to be annealed in order to produce homogeneous samples – with the same properties throughout. At 800 K, Mg₂Si_0.55−xSn_0.4Ge_0.05Bi_x has been reported to have a figure of merit about 1.4, the highest ever reported for these compounds.^[40]

Skutterudite thermoelectrics

Skutterudites have a chemical composition of LM₄X₁₂, where L is a rare-earth metal (optional component), M is a transition metal, and X is a metalloid, a group V element or a pnictogen such as phosphorus, antimony, or arsenic. These materials exhibit ZT>1.0 and can potentially be used in multistage thermoelectric devices.^[41]

Unfilled, these materials contain voids, which can be filled with low-coordination ions (usually rare-earth elements) to reduce thermal conductivity by producing sources for lattice phonon scattering, without reducing electrical conductivity.^[42] It is also possible to reduce the thermal conductivity in skutterudite without filling these voids using a special architecture containing nano- and micro-pores.^[43]

NASA is developing a Multi-Mission Radioisotope Thermoelectric Generator in which the thermocouples would be made of skutterudite, which can function with a smaller temperature difference than the current tellurium designs. This would mean that an otherwise similar RTG would generate 25% more power at the beginning of a mission and at least 50% more after seventeen years. NASA hopes to use the design on the next New Frontiers mission.^[44]

Oxide thermoelectrics

Homologous oxide compounds (such as those of the form (SrTiO
₃)_n(SrO)
_m—the Ruddlesden-Popper phase) have layered superlattice structures that make them promising candidates for use in high-temperature thermoelectric devices.^[45] These materials exhibit low thermal conductivity perpendicular to the layers while maintaining good electronic conductivity within the layers. Their ZT values can reach 2.4 for epitaxial SrTiO
₃ films, and the enhanced thermal stability of such oxides, as compared to conventional high-ZT bismuth compounds, makes them superior high-temperature thermoelectrics.^[46]

Interest in oxides as thermoelectric materials was reawakened in 1997 when a relatively high thermoelectric power was reported for NaCo₂O₄.^[47][46] In addition to their thermal stability, other advantages of oxides are their low toxicity and high oxidation resistance. Simultaneously controlling both the electric and phonon systems may require nanostructured materials. Layered Ca₃Co₄O₉ exhibited ZT values of 1.4–2.7 at 900 K.^[46] If the layers in a given material have the same stoichiometry, they will be stacked so that the same atoms will not be positioned on top of each other, impeding phonon conductivity perpendicular to the layers.^[45] Recently, oxide thermoelectrics have gained a lot of attention so that the range of promising phases increased drastically. Novel members of this family include ZnO,^[46] MnO₂,^[48] and NbO₂.^[49][50]

Cation-substituted copper sulfide thermoelectrics

All variables mentioned are included in the equation for the dimensionless figure of merit, zT, which can be seen at the top of this page. The goal of any thermoelectric experiment is to make the power factor, S² σ, larger while maintaining a small thermal conductivity. This is because electricity is produced through a temperature gradient, so materials that can equilibrate heat very quickly are not useful.^[51] The two compounds detailed below were found to exhibit high-performing thermoelectric properties, which can be evidenced by the reported figure of merit in either respective manuscript.

Cuprokalininite (CuCr₂S₄) is a copper-dominant analogue of the mineral joegoldsteinite. It was recently found within metamorphic rocks in Slyudyanka, part of the South Baikal region of Russia, and researchers have determined that Sb-doped cuprokalininite (Cu_1-xSb_xCr₂S₄) shows promise in renewable technology.^[52] Doping is the act of intentionally adding an impurity, usually to modify the electrochemical characteristics of the seed material. The introduction of antimony enhances the power factor by bringing in extra electrons, which increases the Seebeck coefficient, S, and reduces the magnetic moment (how likely the particles are to align with a magnetic field); it also distorts the crystal structure, which lowers the thermal conductivity, κ. Khan et al. (2017) were able to discover the optimal amount of Sb content (x=0.3) in cuprokalininte in order to develop a device with a ZT value of 0.43.^[52]

Bornite (Cu₅FeS₄) is a sulfide mineral named after an Austrian mineralogist, though it is much more common than the aforementioned cuprokalininite. This metal ore was found to demonstrate an improved thermoelectric performance after undering cation exchange with iron.^[53] Cation exchange is the process of surrounding a parent crystal with an electrolyte complex, so that the cations (positively charged ions) within the structure can be swapped out for those in solution without affecting the anion sublattice (negatively charged crystal network).^[54] What one is left with are crystals that possess a different composition, yet an identical framework. In this way, scientists are granted extreme morphological control and uniformity when generating complicated heterostructures.^[55] As to why it was thought to improve the ZT value, the mechanics of cation exchange often bring about crystallographic defects, which cause phonons (simply put, heat particles) to scatter. According to the Debye-Callaway formalism, a model used to determine the lattice thermal conductivity, κ_L, the highly anharmonic behavior due to phonon scattering results in a large thermal resistance.^[56] Therefore, a greater defect density decreases the lattice thermal conductivity, thereby making a larger figure of merit. In conclusion, Long et al. reported that greater Cu-deficiencies resulted in increases of up to 88% in the ZT value, with a maximum of 0.79.^[57]

The composition of thermoelectric devices can dramatically vary depending on the temperature of the heat they must harvest; considering the fact that more than eighty percent of industry waste falls within a range of 373-575 K, chalcogenides and antimonides are better suited for thermoelectric conversion because they can utilize heat at lower temperatures.^[58] Not only is sulfur the cheapest and lightest chalcogenide, current surpluses may be causing threat to the environment since it is a byproduct of oil capture, so sulfur consumption could help mitigate future damage.^[52] As for the metal, copper is an ideal seed particle for any kind of substitution method because of its high mobility and variable oxidation state, for it can balance or complement the charge of more inflexible cations. Therefore, either the cuprokalininite or bornite minerals could prove ideal thermoelectric components.

Half-Heusler alloys

Half-Heusler (HH) alloys have a great potential for high-temperature power generation applications. Examples of these alloys include NbFeSb, NbCoSn and VFeSb. They have a cubic MgAgAs-type structure formed by three interpenetrating face-centered-cubic (fcc) lattices. The ability to substitute any of these three sublattices opens the door for wide variety of compounds to be synthesized. Various atomic substitutions are employed to reduce the thermal conductivity and enhance the electrical conductivity.^[59]

Previously, ZT could not peak more than 0.5 for p-type and 0.8 for n-type HH compound. However, in the past few years, researchers were able to achieve ZT≈1 for both n-type and p-type.^[59] Nano-sized grains is one of the approaches used to lower the thermal conductivity via grain boundaries- assisted phonon scattering.^[60] Other approach was to utilize the principles of nanocomposites, by which certain combination of metals were favored on others due to the atomic size difference. For instance, Hf and Ti is more effective than Hf and Zr, when reduction of thermal conductivity is of concern, since the atomic size difference between the former is larger than that of the latter.^[61]

Flexible Thermoelectric Materials

Electrically conducting organic materials

Generation of electricity by grabbing both sides of a flexible PEDOT:PSS thermoelectric device

PEDOT:PSS-based model embedded into a glove to generate electricity by body heat

Conducting polymers are of significant interest for flexible thermoelectric development. They are flexible, lightweight, geometrically versatile, and can be processed at scale, an important component for commercialization. However, the structural disorder of these materials often inhibits the electrical conductivity much more than the thermal conductivity, limiting their use so far. Some of the most common conducting polymers investigated for flexible thermoelectrics include poly(3,4-ethylenedioxythiophene) (PEDOT), polyanilines (PANIs), polythiophenes, polyacetylenes, polypyrrole, and polycarbazole. P-type PEDOT:PSS (polystyrene sulfonate) and PEDOT-Tos (Tosylate) have been some of the most encouraging materials investigated. Organic, air-stable n-type thermoelectrics are often harder to synthesize because of their low electron affinity and likelihood of reacting with oxygen and water in the air.^[62] These materials often have a figure of merit that is still too low for commercial applications (~0.42 in PEDOT:PSS) due to the poor electrical conductivity.^[63]

Hybrid Composites Hybrid composite thermoelectrics involve blending the previously discussed electrically conducting organic materials or other composite materials with other conductive materials in an effort to improve transport properties. The conductive materials that are most commonly added include carbon nanotubes and graphene due to their conductivities and mechanical properties. It has been shown that carbon nanotubes can increase the tensile strength of the polymer composite they are blended with. However, they can also reduce the flexibility.^[64] Furthermore, future study into the orientation and alignment of these added materials will allow for improved performance.^[65] The percolation threshold of CNT’s is often especially low, well below 10%, due to their high aspect ratio.^[66] A low percolation threshold is desirable for both cost and flexibility purposes. Reduced graphene oxide (rGO) as graphene-related material was also used to enhance figure of merit of thermoelectric materials.^[67] The addition of rather low amount of graphene or rGO around 1 wt% mainly strengthens the phonon scattering at grain boundaries of all these materials as well as increases the charge carrier concentration and mobility in chalcogenide-, skutterudite- and, particularly, metal oxide-based composites. However, significant growth of ZT after addition of graphene or rGO was observed mainly for composites based on thermoelectric materials with low initial ZT. When thermoelectric material is already nanostructured and possesses high electrical conductivity, such an addition does not enhance ZT significantly. Thus, graphene or rGO-additive works mainly as an optimizer of the intrinsic performance of thermoelectric materials.

Hybrid thermoelectric composites also refer to polymer-inorganic thermoelectric composites. This is generally achieved through an inert polymer matrix that is host to thermoelectric filler material. The matrix is generally nonconductive so as to not short current as well as to let the thermoelectric material dominate electrical transport properties. One major benefit of this method is that the polymer matrix will generally be highly disordered and random on many different length scales, meaning that the composite material will can have a much lower thermal conductivity. The general procedure to synthesize these materials involves a solvent to dissolve the polymer and dispersion of the thermoelectric material throughout the mixture.^[68]

Silicon-germanium alloys

Bulk Si exhibits a low ZT of ~0.01 because of its high thermal conductivity. However, ZT can be as high as 0.6 in silicon nanowires, which retain the high electrical conductivity of doped Si, but reduce the thermal conductivity due to elevated scattering of phonons on their extensive surfaces and low cross-section.^[69]

Combining Si and Ge also allows to retain a high electrical conductivity of both components and reduce the thermal conductivity. The reduction originates from additional scattering due to very different lattice (phonon) properties of Si and Ge.^[70] As a result, Silicon-germanium alloys are currently the best thermoelectric materials around 1000 °C and are therefore used in some radioisotope thermoelectric generators (RTG) (notably the MHW-RTG and GPHS-RTG) and some other high^temperature applications, such as waste heat recovery. Usability of silicon-germanium alloys is limited by their high price and moderate ZT values (~0.7); however, ZT can be increased to 1–2 in SiGe nanostructures owing to the reduction in thermal conductivity.^[71]

Sodium cobaltate

Experiments on crystals of sodium cobaltate, using X-ray and neutron scattering experiments carried out at the European Synchrotron Radiation Facility (ESRF) and the Institut Laue-Langevin (ILL) in Grenoble were able to suppress thermal conductivity by a factor of six compared to vacancy-free sodium cobaltate. The experiments agreed with corresponding density functional calculations. The technique involved large anharmonic displacements of Na
_0.8CoO
₂ contained within the crystals.^[72][73]

Amorphous materials

In 2002, Nolas and Goldsmid have come up with a suggestion that systems with the phonon mean free path larger than the charge carrier mean free path can exhibit an enhanced thermoelectric efficiency.^[74] This can be realized in amorphous thermoelectrics and soon they became a focus of many studies. This ground-breaking idea was accomplished in Cu-Ge-Te,^[75] NbO₂,^[76] In-Ga-Zn-O,^[77] Zr-Ni-Sn,^[78] Si-Au,^[79] and Ti-Pb-V-O^[80] amorphous systems. It should be mentioned that modelling of transport properties is challenging enough without breaking the long-range order so that design of amorphous thermoelectrics is at its infancy. Naturally, amorphous thermoelectrics give rise to extensive phonon scattering, which is still a challenge for crystalline thermoelectrics. A bright future is expected for these materials.

Functionally graded materials

Functionally graded materials make it possible to improve the conversion efficiency of existing thermoelectrics. These materials have a non-uniform carrier concentration distribution and in some cases also solid solution composition. In power generation applications the temperature difference can be several hundred degrees and therefore devices made from homogeneous materials have some part that operates at the temperature where ZT is substantially lower than its maximum value. This problem can be solved by using materials whose transport properties vary along their length thus enabling substantial improvements to the operating efficiency over large temperature differences. This is possible with functionally graded materials as they have a variable carrier concentration along the length of the material, which is optimized for operations over specific temperature range.^[81]

Nanomaterials and superlattices

In addition to nanostructured Bi
₂Te
₃/Sb
₂Te
₃ superlattice thin films, other nanostructured materials, including silicon nanowires,^[69] nanotubes and quantum dots show potential in improving thermoelectric properties.

Tin selenide

In 2014, researchers at Northwestern University discovered that tin selenide (SnSe) has a ZT of 2.6 along the b axis of the unit cell.^[95][96] This was the highest value reported to date. This was attributed to an extremely low thermal conductivity found in the SnSe lattice. Specifically, SnSe demonstrated a lattice thermal conductivity of 0.23 W·m⁻¹·K⁻¹, much lower than previously reported values of 0.5 W·m⁻¹·K⁻¹ and greater.^[97] This material also exhibited a ZT of 2.3±0.3 along the c-axis and 0.8±0.2 along the a-axis. These results were obtained at a temperature of 923 K (650 °C). As shown by the figures below, SnSe performance metrics were found to significantly improve at higher temperatures; this is due to a structural change. Power factor, conductivity, and thermal conductivity all reach their optimal values at or above 750 K, and appear to plateau at higher temperatures. However, other groups have not been able to reproduce the reported bulk thermal conductivity data.^[98]

SnSe performance metrics^[97]

Although it exists at room temperature in an orthorhombic structure with space group Pnma, SnSe undergoes a transition to a structure with higher symmetry, space group Cmcm, at higher temperatures.^[99] This structure consists of Sn-Se planes that are stacked upwards in the a-direction, which accounts for the poor performance out-of-plane (along a-axis). Upon transitioning to the Cmcm structure, SnSe maintains its low thermal conductivity but exhibits higher carrier mobilities.^[97]

One impediment to further development of SnSe is that it has a relatively low carrier concentration: approximately 10¹⁷ cm⁻³. Compounding this issue is the fact that SnSe has been reported to have low doping efficiency.^[100]

However, such single crystalline materials suffer from inability to make useful devices due to their brittleness as well as narrow range of temperatures, where ZT is reported to be high.

In 2021 the researchers announced a polycrystalline form of SnSe that was at once less brittle and featured a ZT of 3.1.^[101]

Anderson localization

Anderson localization is a quantum mechanical phenomenom where charge carriers in a random potential are trapped in place (i.e. they are in localized states as opposed to being in scattering states if they could move freely).^[102] This localization prevents the charge carriers from moving, which inhibits their contribution to the thermal conductivity of a material, but because it also lowers the electrical conductivity, it was thought to reduce ZT and be detrimental for thermoelectric materials.^[103][104] In 2019, it was proposed that by localizing only the minority charge carriers in a doped semiconductor (i.e. holes in an n-doped semiconductor or electrons in a p-doped semiconductor), Anderson localization could increase ZT. The heat conductivity associated with movement of the minority charge carriers would be reduced while electrical conductivity of the majority charge carrier would be unaffected.^[105]

In 2020, researchers at Kyung Hee University demonstrated the use of Anderson localization in an n-type semiconductor to improve the thermoelectric properties of a material. They embedded nanoparticles of silver telluride (Ag₂Te) in a lead telluride (PbTe) matrix. Ag₂Te undergoes a phase transition around 407 K. Below this temperature, both holes and electrons are localized at the Ag₂Te nanoparticles, while after the transtion, holes are still localized, but electrons can move freely in the material. The researchers were able to increase ZT from 1.5 to above 2.0 using this method.^[106]

3D Printing

Significant improvement on 3D printing skills has made it possible for thermoelectric components to be prepared via 3D printing. Thermoelectric products are made from special materials that absorb heat and create electricity. The requirement of fitting complex geometries in tightly constrained spaces makes 3D printing the ideal manufacturing technique.^[109] There are several benefits to the use of additive manufacturing in thermoelectric material production. Additive manufacturing allows for innovation in the design of these materials, facilitating intricate geometries that would not otherwise be possible by conventional manufacturing processes. It reduces the amount of wasted material during production and allows for faster production turnaround times by eliminating the need for tooling and prototype fabrication, which can be time-consuming and expensive.^[110]

There are several major additive manufacturing technologies that have emerged as feasible methods for the production of thermoelectric materials, including continuous inkjet printing, dispenser printing, screen printing, stereolithography, and selective laser sintering. Each method has its own challenges and limitations, especially related to the material class and form that can be used. For example, selective laser sintering (SLS) can be used with metal and ceramic powders, stereolithography (SLA) must be used with curable resins containing solid particle dispersions of the thermoelectric material of choice, and inkjet printing must use inks which are usually synthesized by dispersing inorganic powders to organic solvent or making a suspension.^[111][112]

The motivation for producing thermoelectrics by means of additive manufacturing is due to a desire to improve the properties of these materials, namely increasing their thermoelectric figure of merit ZT, and thereby improving their energy conversion efficiency.^[113] Research has been done proving the efficacy and investigating the material properties of thermoelectric materials produced via additive manufacturing. An extrusion-based additive manufacturing method was used to successfully print bismuth telluride (Bi₂Te₃) with various geometries. This method utilized an all-inorganic viscoelastic ink synthesized using Sb₂Te₂ chalcogenidometallate ions as binders for Bi₂Te₃-based particles. The results of this method showed homogenous thermoelectric properties throughout the material and a thermoelectric figure of merit ZT of 0.9 for p-type samples and 0.6 for n-type samples. The Seebeck coefficient of this material was also found to increase with increasing temperature up to around 200 °C.^[114]

Groundbreaking research has also been done towards the use of selective laser sintering (SLS) for the production of thermoelectric materials. Loose Bi₂Te₃ powders have been printed via SLS without the use of pre- or post-processing of the material, pre-forming of a substrate, or use of binder materials. The printed samples achieved 88% relative density (compared to a relative density of 92% in conventionally manufactured Bi₂Te₃). Scanning Electron Microscopy (SEM) imaging results showed adequate fusion between layers of deposited materials. Though pores existed within the melted region, this is a general existing issue with parts made by SLS, occurring as a result of gas bubbles that get trapped in the melted material during its rapid solidification. X-ray diffraction results showed that the crystal structure of the material was intact after laser melting.

The Seebeck coefficient, figure of merit ZT, electrical and thermal conductivity, specific heat, and thermal diffusivity of the samples were also investigated, at high temperatures up to 500 °C. Of particular interest is the ZT of these Bi₂Te₃ samples, which were found to decrease with increasing temperatures up to around 300 °C, increase slightly at temperatures between 300-400 °C, and then increase sharply without further increase in temperature. The highest achieved ZT value (for an n-type sample) was about 0.11.

The bulk thermoelectric material properties of samples produced using SLS had comparable thermoelectric and electrical properties to thermoelectric materials produced using conventional manufacturing methods. This the first time the SLS method of thermoelectric material production has been used successfully.^[113]

Thermomechanical Stresses in Thermoelectric Devices^[115]

Refrigeration

Thermoelectric materials can be used as refrigerators, called "thermoelectric coolers", or "Peltier coolers" after the Peltier effect that controls their operation. As a refrigeration technology, Peltier cooling is far less common than vapor-compression refrigeration. The main advantages of a Peltier cooler (compared to a vapor-compression refrigerator) are its lack of moving parts or refrigerant, and its small size and flexible shape (form factor).^[132]

The main disadvantage of Peltier coolers is low efficiency. It is estimated that materials with ZT>3 (about 20–30% Carnot efficiency) would be required to replace traditional coolers in most applications.^[82] Today, Peltier coolers are only used in niche applications, especially small scale, where efficiency is not important.^[132]

Power generation

Thermoelectric efficiency depends on the figure of merit, ZT. There is no theoretical upper limit to ZT, and as ZT approaches infinity, the thermoelectric efficiency approaches the Carnot limit. However, until recently no known thermoelectrics had a ZT>3.^[133] In 2019, researchers reported a material with approximated ZT between 5 and 6.^[134][135]

As of 2010, thermoelectric generators serve application niches where efficiency and cost are less important than reliability, light weight, and small size.^{[136] [137]}

Internal combustion engines capture 20–25% of the energy released during fuel combustion.^{[136] [138]} Increasing the conversion rate can increase mileage and provide more electricity for on-board controls and creature comforts (stability controls, telematics, navigation systems, electronic braking, etc.)^[139] It may be possible to shift energy draw from the engine (in certain cases) to the electrical load in the car, e.g., electrical power steering or electrical coolant pump operation.^[136][138]

Cogeneration power plants use the heat produced during electricity generation for alternative purposes; being this more profitable in industries with high amounts of waste energy.^[136]

Thermoelectrics may find applications in such systems or in solar thermal energy generation.^{[136] [140]}